Amazing Enamel Effects

Buying a kiln recently has given me the chance to experiment with enamelling on larger pieces of copper and to produce some really cool effects. These effects happen when you combine different types of enamel.

I usually use smaller flat pieces of copper for making enamelled earrings and have had some of these effects happen when firing with a torch but they are much more obvious when you use larger pieces. I made a few practice pieces which you can see in the photos below.



This was flux {a transparent enamel not to be confused with soldering flux!} applied straight onto copper and fired until the copper was a bright golden colour. Then I added a layer of liquid enamel in green and red over the flux and fired again. 
The lines and spots form when the enamel becomes hot enough to start moving and in this case the transparent pushes through the liquid enamel layer forming these cool lines and spots. The effect is better in the green liquid enamel than the red. 


Next is an effect that reminds me of raku fired ceramics.



This time I applied a layer of black opaque enamel and fired until it was almost smooth. Then a layer of white liquid enamel was applied on top and fully fired to produce this fab effect. 



I think the lines are formed through movement in the liquid enamel layer allowing the black base to show through. They aren't cracks in the white enamel as when it's fully fired the enamel surface is completely smooth. 

It's difficult to achieve an even layer of the liquid enamel on a sloped surface like this bowl so it is a bit darker in places. Allowing the first liquid layer to dry then applying another layer is also quite hard to do evenly! I've found it's better to fire just once for the best effect. You can fire it twice using two layers of the liquid enamel but you do get the crack effect happening in both layers which overlaps and doesn't look as good. I think some experimenting is called for to get it right :D

The next effect uses a base of opaque enamel then a layer of clear flux. The top layer is a liquid enamel.



This is the same as the first example but with added colour by using a base of opaque orange underneath the clear flux. The green liquid layer has two layers on the right side and the liquid layer was fired just once.



There is a bit more going on where there is just the one layer of liquid enamel but the other side still looks interesting. I think the shape of the piece you use will affect the patterns formed too.

The next effect is my favourite, probably because it's so colourful.



This effect was produced by layering a transparent enamel between two opaques. Gravity and the sloping sides of the bowl also help to create the effect.



When it's fired to 800°C the transparent enamel layer starts to push through the top opaque layer creating cell shapes. This allows the base opaque colour to show through too. 
In this case I used an opaque seafoam base, a turquoise transparent and an opaque pea green top layer.

This bowl is made the same way with slightly different shades of blue and green opaque colours and I added some holes for decoration. 


I love the way the top hole has stretched into an oval shape as I formed the bowl.


I already have a list of colour combinations to try when I make some more of these :D

I still have a lot more to learn with kiln firing enamels but these practice pieces are really helping me to discover the wonderful effects you can achieve with enamel.



Copyright © 2017 Cinnamon Jewellery. All rights reserved.

Comments

  1. All the pieces are super duper gorgeous making me wish that I could play with Enamel here. The photos look fanstastic on this new, clean white layout

    ReplyDelete
  2. Your "raku" piece looks very interesting, and the green ones too! I have never tried mixing types of enamel the way you do. Time to start I think. About liquid enamels I can tell they are often the "hardest" to fire.

    ReplyDelete
    Replies
    1. I love the "raku" effect too. I'm finding that liquid enamels are sometimes a bit temperamental to use but I am enjoying trying things with them.

      Delete
    2. At last I've found the enamel of my dreams! Ive seen it in alot off pictures but never found it. At least I believe that.... Goldfoil is very expensive, but this is to be found at http://www.vitrumsignum.com/enamels/wet-process-for-copper-and-steel/11817-metallic-gold/

      Delete
    3. That metallic gold enamel looks like something I need to try! Thanks for the link :D

      Delete
    4. Youre still a member of the EU I hope...? ;)

      Delete
    5. Waiting for an enamel of my dreams with.... a newly broken arm. :(

      Delete
    6. Oh no! That must be really frustrating. Hope it gets better quickly :D

      Delete
  3. Wow! These are so cool Tracy! It looks like you are having so much fun with the kiln. Your favorite piece is mine too. It reminds me of a peacock since those colors are dominant in their feathers. Such pretty color choices.

    ReplyDelete
  4. Tracy thanks so much for sharing! I've been trying to get that cell effect for awhile now. I too am experimenting but I haven't really delved into the liquid enamels. Do you buy the powdered form or liquid? I am just now going to experiment with liquid enamel. All I have at this moment is white. It's almost like playing with pottery! :D

    ReplyDelete
  5. Ooops....meant to mention that I too notice that different enamels react differently too each other. It must have to do with the coefficient expansion of each enamel. There is so much to learn. Your sample of the cell effect, was that using liquid or powder?

    ReplyDelete
    Replies
    1. Hi Kalaya,
      Using liquid enamels does make me think of ceramic glazes and it feels a bit "free-er" {is that a word?} to use than powders. Most of the liquid enamels I have are powders that I mix myself but I recently bought a couple already mixed. There's not much difference apart from the price and convenience. I like the fact you can mix the liquids and make new colours.
      The effects are definitely because of the different CoE of the enamels which I know very little about :D

      The cell effect is done with powder enamels and gets better the longer you fire.

      Delete
    2. Free-er. Well then I will have to expand on my liquid then. :D Do you have any tips on mixing? I find it a tad difficult. I mix it with distilled water to a sort of pancake consistency. water first then powder.

      Delete
    3. I usually add the distilled water to the powder and mix with a stick or plastic spoon. There is a knack to getting the right consistency which I don't always get :D I try to go for single cream consistency which is quite runny but if it doesn't work I wash it off the piece then either add more powder or water to the mix to get it right.

      I do get small lumps in the mix sometimes so I just remove them if I see them on the piece. I probably should spend more time mixing but I get impatient and just want to start :D

      Delete
    4. Merci Tracy! I get impatient as well. :)

      Delete
  6. Very cool! I haven't used liquid enamels at all, looks like I should give them a try. Love what you're doing! I really enjoy your blog, thanks for posting!

    ReplyDelete
  7. Oh my word those cells you got on those bowls are delicious! Your experimenting with enamels makes me feel like getting mine out for a play again! I really need to stop buying other art supplies and get myself a Kiln once and for all!

    ReplyDelete
    Replies
    1. I'm really glad I have mine at last. It could do with it being a bit bigger to make things easier with larger pieces but I can manage with it for what I want to do :D

      Delete
  8. so you put these in the kiln? i'm loving this idea? what kind of kiln did you get?

    ReplyDelete
    Replies
    1. It's a Prometheus Pro 1, not programmable but fine for enamelling small items.

      Delete
  9. So glad I found your site, these are a-m-a-z-i-n-g! What flux did you use? I tried with trans.for silver and 2010 but nothing happened :( Trying to learn liquid enameling, but find it hard to get the surface even, especially with the crackeling-effect. Do your liquid enamel get as glossy as the powder does?

    ReplyDelete
  10. Wow, these all looks so awesome. Thanks for showcasing.

    ReplyDelete
  11. Looks so pretty! making such beautiful pieces, surely will be satisfying in itself. Isn't it?

    ReplyDelete
  12. These are such gorgeous pieces! I love them!

    ReplyDelete
  13. Thanks very much..I got the transparent between opaques effect by accident and have been trying to figure out how I did it as was just experimenting with different enamels...now I know!

    ReplyDelete
  14. What line of enamels are you using -- Ball, Milton Bridge (Schauer), Thompson ... ? Different enamel mfgs have slightly different COEs/.

    ReplyDelete
    Replies
    1. They are mostly Thompson and WG Ball. The liquid enamels I use are from WG Ball too.

      Delete
  15. For your favorite effect are you layering all three layers dry and then firing or do you fire each layer?

    ReplyDelete
    Replies
    1. Hi, thanks for your comment. Each layer is fired separately.

      Delete

Post a Comment

Your comments and questions are very welcome!
If you would prefer to contact me directly please use the contact form on my "get in touch" page.

Popular posts from this blog

Combining Soldering And Enamel

The need to make cute, brightly coloured enamel studs propelled me into the world of combining soldering with enamel a couple of years ago. I knew from reading up on it that it was possible to enamel and solder on the same piece but wasn't too confident I was able to do it back then. It was a slightly embarrassing occurance that made me just get on with - I'd made some enamel studs with glued on stud posts. I'd used 2 part epoxy resin which was a job in itself as it set hard after 5 minutes so I had to keep mixing more up. The finished studs looked ok but that little voice in my head kept asking "are you sure you want to use glue?" I wasn't but didn't think I had any other way to do it so I used glue. I sold my first pair and merrily sent them on their way to Canada. A couple of week later the buyer got in touch to say the stud post had come off one of the earrings and the other was hanging off. I was mortified, apologized profusely and refunded her m

Etching Silver Using Nail Art Stamps

So my love/hate relationship with etching sterling silver continues. I've tried a few times now and always end up with different results most of them not that great to be honest. I've tried connecting the silver and a piece of copper to a 9v battery and also heating the ferric nitrate. Sometimes the results are good sometimes not so good. I currently have an etched piece of silver sheet waiting to be reticulated and rid it of the mess that is the etched "pattern".  I now know that using stamps and Stayz On ink just doesn't work with silver - the time needed to etch using ferric nitrate is much longer than etching copper and the ink starts to wear away after about an hour. This results in the pattern being patchy as the resist is eaten away and the silver ends up quite lumpy and course looking. I have yet to try using pnp paper. I don't know why but it all seems a bit of a faff to do. I don't have a laser printer so would need to find somewhere or

Embossing Metal With My Sizzix Bigshot

I must admit up until a few weeks ago I was vaguely familiar with the name Sizzix but as to what you actually did with a "Sizzix" I was completely in the dark! That was until I stumbled across a video from Vintaj showing how you could use their embossing folders with a Bigshot to create designs on metal ("metal" - my favourite word after chocolate!) I was really impressed and itching to have a go, I just needed a Bigshot........ I waited a few weeks then when the urge to possess one overcame me I went out debit card at the ready..............and the shop had sold out! So I trundled off to The Range on the off chance and came home clutching my own surprisingly heavy pink and black wonder machine. It sat on the dining room table for a couple of days while I waited for the embossing folders I'd ordered online to arrive then the time came to start playing! I started with some pre-cut 24g copper hearts and the Wildflower Vines and the Butterfly Swirls Deco