What I've Been Doing Lately...Etched Bangles


One of the joys I've found with making bangles is the infinite variety of designs you can make. I use a lot of copper for bangles and up to fairly recently most of my designs have been made from round wire that I've hammered. It wasn't until I had a custom request for a "bark" texture bangle in sterling {think flattened shape with hammered line marks} that I made my first flat bangle.

Having a flat surface gives you more options for design so I decided to try some etched patterns on the flat style bangles.

I started with lengths of the round copper wire which I annealed to soften it then rolled it through the rolling mill until it was flat enough for what I wanted to do.




I then annealed the flattened wire and straightened it on a steel block before cutting it to size and filing the ends flat




The bangles ready for soldering.


After soldering the bangles, cleaning up and shaping them the next step was to apply the resist on the areas of the bangle I didn't want to etch. I used a Sharpie and covered the inside of the bangles and then around the edges.


I'd never etched anything with a solder join before so I made sure the solder join on the bangles was covered with the Sharpie too. I didn't take any photos of the "design" part but I basically drew lines in different thicknesses on the front of the bangles with the Sharpie.


 I also tried another way to etch the bangles by applying the resist before the bangle was soldered. Having the metal flat worked better for the stamped designs as it was impossible to stamp the formed bangles without the ink smudging and it looking a bit of a mess - so I did it on the flat piece of metal and soldered the bangle afterwards. The only drawback with doing it that way is you remove some of the etched design when you're cleaning up the solder join.

I forgot to photograph the etching bit {sorry!} but I etched the copper for about 30 minutes. The time it takes to etch depends on how fresh your ferric chloride is and how deep you like to etch.


Cleaning off the Sharpie marks after etching.


The cleaned up bangle.


I then oxidized the bangles and cleaned them up with wire wool. I also tried using vinyl stickers as the resist on some of the bangles. I liked the subtle effect of their patterns. The zigzag {2nd left} is my favourite.



Overall I like the "stripe" design best. It was fairly time consuming to do but I love it's rustic charm. 


I think I could achieve a similar look without etching and doing lots of tedious  er....fun..... colouring in with Sharpie pens. The rolling mill and some thin gauge wire beckons......




Copyright © 2015 Cinnamon Jewellery. All rights reserved.

Comments

  1. I love all the textures you created! The step by step photos are really cool to see.

    ReplyDelete
  2. Beautiful! I work with silver and have been wanting to play with copper...I think you've inspired me to go for it!
    Judypimperl.blogspot.com

    ReplyDelete
    Replies
    1. Thanks Judy! Copper's great to work with and much cheaper than silver :D

      Delete
  3. I have been wanting to make etched bracelet and pendants too, bought all the supplies, but never tried.

    ReplyDelete
    Replies
    1. Have a go Divya, you'll love how easy it is to do and the results!

      Delete
  4. A question: How did you suspend the bracelets in the etching solution?

    ReplyDelete
    Replies
    1. I used a shallow dish for the etching solution and just let the bangles sit on the bottom. I swished the solution about a few times and turned the bangles over a couple of times.

      Delete
  5. Tracy, I've been struggling with soldering copper for rings and bangles. I bought copper solder, but it is so brittle, it sometimes breaks under the hammer. What kind of solder do you use for these gorgeous copper bangles??

    ReplyDelete
    Replies
    1. Hi Jane, thanks for your comment!
      I use normal silver solder then file and sand the solder join so it becomes a thin silver line that's not really that noticeable. I have tried copper solder but I found it extremely hard to cut. I like to clean up my solder joins as much as possible but found the copper colour in copper solder wears off when you sand it leaving a gray colour so I stuck to using silver solder :D

      Delete

Post a Comment

Your comments and questions are very welcome!
If you would prefer to contact me directly please use the contact form on my "get in touch" page.

Popular posts from this blog

Combining Soldering And Enamel

The need to make cute, brightly coloured enamel studs propelled me into the world of combining soldering with enamel a couple of years ago. I knew from reading up on it that it was possible to enamel and solder on the same piece but wasn't too confident I was able to do it back then. It was a slightly embarrassing occurance that made me just get on with - I'd made some enamel studs with glued on stud posts. I'd used 2 part epoxy resin which was a job in itself as it set hard after 5 minutes so I had to keep mixing more up. The finished studs looked ok but that little voice in my head kept asking "are you sure you want to use glue?" I wasn't but didn't think I had any other way to do it so I used glue. I sold my first pair and merrily sent them on their way to Canada. A couple of week later the buyer got in touch to say the stud post had come off one of the earrings and the other was hanging off. I was mortified, apologized profusely and refunded her m

Etching Silver Using Nail Art Stamps

So my love/hate relationship with etching sterling silver continues. I've tried a few times now and always end up with different results most of them not that great to be honest. I've tried connecting the silver and a piece of copper to a 9v battery and also heating the ferric nitrate. Sometimes the results are good sometimes not so good. I currently have an etched piece of silver sheet waiting to be reticulated and rid it of the mess that is the etched "pattern".  I now know that using stamps and Stayz On ink just doesn't work with silver - the time needed to etch using ferric nitrate is much longer than etching copper and the ink starts to wear away after about an hour. This results in the pattern being patchy as the resist is eaten away and the silver ends up quite lumpy and course looking. I have yet to try using pnp paper. I don't know why but it all seems a bit of a faff to do. I don't have a laser printer so would need to find somewhere or

Embossing Metal With My Sizzix Bigshot

I must admit up until a few weeks ago I was vaguely familiar with the name Sizzix but as to what you actually did with a "Sizzix" I was completely in the dark! That was until I stumbled across a video from Vintaj showing how you could use their embossing folders with a Bigshot to create designs on metal ("metal" - my favourite word after chocolate!) I was really impressed and itching to have a go, I just needed a Bigshot........ I waited a few weeks then when the urge to possess one overcame me I went out debit card at the ready..............and the shop had sold out! So I trundled off to The Range on the off chance and came home clutching my own surprisingly heavy pink and black wonder machine. It sat on the dining room table for a couple of days while I waited for the embossing folders I'd ordered online to arrive then the time came to start playing! I started with some pre-cut 24g copper hearts and the Wildflower Vines and the Butterfly Swirls Deco