A New Copper Loop Bangle And How I Made It


I started making copper bangles sort of by accident. I had some thick gauge copper wire and didn't know what to do one night at a jewellery class I was at so decided to experiment. And I haven't looked back. They have proved to be very popular especially with men buying gifts for their copper wedding anniversary -  usually leaving it to the last minute! 

So it makes sense to expand on the designs I make which is why I experimented with this loop bangle recently. I cut a length of 2.6mm {10g} round copper wire and annealed it so it would be easier to shape. I guessed the length I would need - I had no idea how long the wire would need to be at this point. I used a bezel mandrel to form the loops starting at the centre point of the wire.


I had enough wire to form six loops with some left for the straight section. I annealed the wire again and hammered the curved sections then used a texturing hammer to add some pattern to the loops and the straight wire.


The next step was to solder the loops at the point where they touched each other. This would give the bangle stability. Without thinking I bent the ends of the wire up then realized I'd bent them the wrong way! I wanted to solder on the back of the loops {what would become the inside of the bangle} to minimize the amount of solder getting onto the front textured side of the wire. * I've since realized I didn't need to bend the ends of the wire at all, I can still solder the loops with the straight bits sticking out at either end!* ** Edited {again!} to add the reason I bent the wires in the first place was so the bangle would fit in my pickle pot - I knew there was a reason :D

I overcame my slightly senile moment by building a mini mountain from broken bits of soldering block so the wire ends could hang over the edges.


After soldering. 
A bit of clean up to do but most of it's on the smooth side so not too difficult to do.


After cleaning up the solder joins I straightened the wire and cut the bangle the right length for a medium size.

  
Flux applied and ready for soldering the join.


The bangle cleaned up and shaped before oxidizing in LOS.

 It was the prototype after all and it would look better with another loop. I always think an odd number looks better than an even number with things decorative. I've worked out the length of wire I need to start with to allow for that plus next time I need the get the loops a bit more upright and graduated in size which will hopefully stop the bangle sitting at an angle as much.

But for a first attempt I'm happy with it and it's just been listed on Etsy. I can see a few decorative options for the design too - I'm thinking silver balls and possibly coils.... :D


Hallmarked!
A bit late but this is the hallmark for my sterling silver bangles! I was so excited to see it when my bangles arrived back from the London Assay Office. I asked for a 3D laser mark as big as they thought suitable as my stamp is quite small at 0.75mm. I'm pleased to say I've sold a few of the hallmarked bangles too!





Copyright © 2015 Cinnamon Jewellery. All rights reserved.

Comments

  1. When I see this bangle I am reminded of the armlets/bands that greeks/romans used to wear - for power and for protection

    ReplyDelete
  2. Nice work with the copper! It is such a gorgeous metal that is easy to work with and very affordable. Your hallmark stamp is awesome! Congratulations. It must be an amazing feeling to have your stamp put on your work.

    ReplyDelete
  3. Brava Tracy! Questo è bello, ma sono sicura che farai altre variante meravigliose. Belli anche i tuoi punzoni personaizzati!!!

    ReplyDelete
    Replies
    1. Grazie Monica! The design still needs tweaking but I will no doubt add some decoration to the copper loops at some point :D

      Delete
  4. Lovely, bold bangle, sure it will prove popular :)
    Heather

    ReplyDelete
  5. Replies
    1. Thank you Kalaya! There is a new improved version too :D

      Delete
  6. Replies
    1. Thanks for your comment Michelle, I love that colour too :D

      Delete
  7. Love your hallmark! I wish we had that over here, but at the same time it's nice to not have to worry about it too. But I love that your pieces are easily traced back to the maker that way!

    ReplyDelete
    Replies
    1. Thanks Em! Yes it is nice having a hallmark with my initials in there too but also a bit of a pain!

      Delete
  8. I never thought it would be that easy! Thanks for the lovely piece of writing! I also like blog posts from Mishalam they are also quite informative.

    ReplyDelete

Post a Comment

Your comments and questions are very welcome!
If you would prefer to contact me directly please use the contact form on my "get in touch" page.

Popular posts from this blog

Combining Soldering And Enamel

The need to make cute, brightly coloured enamel studs propelled me into the world of combining soldering with enamel a couple of years ago. I knew from reading up on it that it was possible to enamel and solder on the same piece but wasn't too confident I was able to do it back then. It was a slightly embarrassing occurance that made me just get on with - I'd made some enamel studs with glued on stud posts. I'd used 2 part epoxy resin which was a job in itself as it set hard after 5 minutes so I had to keep mixing more up. The finished studs looked ok but that little voice in my head kept asking "are you sure you want to use glue?" I wasn't but didn't think I had any other way to do it so I used glue. I sold my first pair and merrily sent them on their way to Canada. A couple of week later the buyer got in touch to say the stud post had come off one of the earrings and the other was hanging off. I was mortified, apologized profusely and refunded her m

Etching Silver Using Nail Art Stamps

So my love/hate relationship with etching sterling silver continues. I've tried a few times now and always end up with different results most of them not that great to be honest. I've tried connecting the silver and a piece of copper to a 9v battery and also heating the ferric nitrate. Sometimes the results are good sometimes not so good. I currently have an etched piece of silver sheet waiting to be reticulated and rid it of the mess that is the etched "pattern".  I now know that using stamps and Stayz On ink just doesn't work with silver - the time needed to etch using ferric nitrate is much longer than etching copper and the ink starts to wear away after about an hour. This results in the pattern being patchy as the resist is eaten away and the silver ends up quite lumpy and course looking. I have yet to try using pnp paper. I don't know why but it all seems a bit of a faff to do. I don't have a laser printer so would need to find somewhere or

Embossing Metal With My Sizzix Bigshot

I must admit up until a few weeks ago I was vaguely familiar with the name Sizzix but as to what you actually did with a "Sizzix" I was completely in the dark! That was until I stumbled across a video from Vintaj showing how you could use their embossing folders with a Bigshot to create designs on metal ("metal" - my favourite word after chocolate!) I was really impressed and itching to have a go, I just needed a Bigshot........ I waited a few weeks then when the urge to possess one overcame me I went out debit card at the ready..............and the shop had sold out! So I trundled off to The Range on the off chance and came home clutching my own surprisingly heavy pink and black wonder machine. It sat on the dining room table for a couple of days while I waited for the embossing folders I'd ordered online to arrive then the time came to start playing! I started with some pre-cut 24g copper hearts and the Wildflower Vines and the Butterfly Swirls Deco